The glass transition temperature of iron and titanium containing phosphate based glasses
In this study various compositions in the phosphate based glass (PBG) system of (50-x)P2O5-40Ca- (5+x)Na-5TiO2 and (50-x)P2O5-40Ca-(5+x)Na-5Fe2O3, where x= 5 and 10 were investigated for glass transition temperature (Tg) via thermo mechanical analyser (TMA) and differential scanning calorimetry (...
Saved in:
| Main Authors: | , , , , |
|---|---|
| 格式: | Article |
| 语言: | English |
| 出版: |
Trans Tech Publications Ltd., Switzerland
2015
|
| 主题: | |
| 在线阅读: | http://irep.iium.edu.my/48557/ http://irep.iium.edu.my/48557/ http://irep.iium.edu.my/48557/ http://irep.iium.edu.my/48557/1/The_glass_transition_temperature_of_iron_and_titanium_containing_phosphate_based_glasses.pdf |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| 总结: | In this study various compositions in the phosphate based glass (PBG) system of (50-x)P2O5-40Ca-
(5+x)Na-5TiO2 and (50-x)P2O5-40Ca-(5+x)Na-5Fe2O3, where x= 5 and 10 were investigated for
glass transition temperature (Tg) via thermo mechanical analyser (TMA) and differential scanning
calorimetry (DSC). The amorphous nature of the glasses was confirmed via XRD. The Tg measured
via DSC was consistently higher by 19°C-29°C compared to TMA and was due to the thermal
history and the heating rate of the samples. The Tg increased with increasing phosphate content in
both glass systems. The Tg for Ti containing PBG was found to be in the range of 453°C-500°C
whilst Tg for Fe containing PBG was in the range of 449°C-494°C. Consistently higher Tg for the Ti
containing glass series compared to the Fe containing glasses may be attributed to the smaller ionic
radius and therefore higher field strength of Ti4+
.
|
|---|