Surface breakdown property of SiO2 added MgO under electron bombardment in vacuum: a promising materials for spacecraft and space station
A surface breakdown (flashover) might occur on the surface of an insulator when it was bombarded by electron beam until exceeding a critical value. The strength of SiO2 added MgO to withstand flashover treeing appearance was evaluated by bombarding the samples by 25 keV electron beam generated by a...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Article |
| 语言: | English |
| 出版: |
SENTRA Academic Publishers
2007
|
| 主题: | |
| 在线阅读: | http://irep.iium.edu.my/8677/ http://irep.iium.edu.my/8677/1/AGUS_-_Canadian_Journal_of_Pure_and_Applied_Sciences_2007.pdf |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| 总结: | A surface breakdown (flashover) might occur on the surface of an insulator when it was bombarded by electron beam until exceeding a critical value. The strength of SiO2 added MgO to withstand flashover treeing appearance was evaluated by bombarding the samples by 25 keV electron beam
generated by a scanning electron microscope. There was a significant increase of bombardment-time to initiate surface breakdown when SiO2 addition was 6 wt%. This compound was about 5 times better in withstanding breakdown compared with materials commonly used in spacecraft
such as teflon, kapton and milar materials. It could be considered that 6 wt% SiO2 added MgO became a promising material for spacecraft and space station where space radiation may damage spacecraft body or influence the communication system. |
|---|