Characterisation of Li2SnO3 by solution evaporation method using nitric acid as chelating agent
Lithium stannate (Li2SnO3) was prepared by solution evaporation method utilising acetates of tin and lithium as starting materials. From thermogravimetric analysis, no weight loss was observed at temperatures above 800 degrees C. The Li2SnO3 precursor was then sintered at 800 degrees C for 5, 6, 7,...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Published: |
2011
|
| Subjects: | |
| Online Access: | http://www.ingentaconnect.com/content/maney/mri/2011/00000015/A00201s2/art00032?token=005517caf510dcb405847447b49792f2a3142427c3a63523b33757e6f3f2f2730673f582f6b5b350643e7 http://www.ingentaconnect.com/content/maney/mri/2011/00000015/A00201s2/art00032?token=005517caf510dcb405847447b49792f2a3142427c3a63523b33757e6f3f2f2730673f582f6b5b350643e7 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Internet
http://www.ingentaconnect.com/content/maney/mri/2011/00000015/A00201s2/art00032?token=005517caf510dcb405847447b49792f2a3142427c3a63523b33757e6f3f2f2730673f582f6b5b350643e7http://www.ingentaconnect.com/content/maney/mri/2011/00000015/A00201s2/art00032?token=005517caf510dcb405847447b49792f2a3142427c3a63523b33757e6f3f2f2730673f582f6b5b350643e7