Solidification analysis in permanent mould casting of aluminium alloy LM6 reinforced titanium carbide particulates metal matrix composites
Permanent mould casting was used as the production technique to produce the metal matrix composites (MMCs) specimens. Thermal measurements during the casting process were recorded. Based on these data, solidification graphs were plotted to understand the solidification characteristics. Solidificatio...
Disimpan dalam:
| Pengarang-pengarang Utama: | , |
|---|---|
| Format: | Conference or Workshop Item |
| Diterbitkan: |
Trans Tech Publications Ltd
2017
|
| Subjek-subjek: | |
| Capaian Atas Talian: | https://www.scientific.net/MSF.889.148 https://www.scientific.net/MSF.889.148 http://umpir.ump.edu.my/14385/1/Solidification%20Analysis%20in%20Permanent%20Mould%20Casting%20of%20Aluminium%20Alloy%20LM6%20ReinforcedTitanium%20Carbide%20Particulates%20Metal%20Matrix%20Composites.pdf http://umpir.ump.edu.my/14385/7/33.%20Solidification%20Analysis%20in%20Permanent%20Mould%20Casting%20of%20Aluminium%20Alloy%20LM6%20Reinforced%20Titanium%20Carbide%20Particulates%20Metal%20Matrix%20Composites.pdf |
| Penanda-penanda: |
Tambah Penanda
Tiada Penanda, Jadilah orang pertama menanda rekod ini!
|
| Ringkasan: | Permanent mould casting was used as the production technique to produce the metal matrix composites (MMCs) specimens. Thermal measurements during the casting process were recorded. Based on these data, solidification graphs were plotted to understand the solidification characteristics. Solidification analysis was performed by interpreting the parameters drawn from the solidification graphs. Parameters such as; nucleation primary alpha phase temperature, liquidus arrest temperature, eutectic growth temperature and solidification time were identified. The results showed that addition of titanium carbide particulates (TiCp) into the aluminium-11.8% silicon alloy (LM6) have affected various time and temperature parameters of its solidification properties. These in turn will have an influence on the mechanical property of the MMCs. |
|---|