Preparation and characterization of cobalt- zinc catalyst SBA 15 supported for fischer-tropsch synthesis: effect on zinc loading
The influence of promoter (Zn) on the physiochemical and catalytic properties of mesaporous silica Co/SBA-15 catalysts for the Fischer-Tropsch (FT) synthesis was investigated. SBA-15 was synthesized as support. The mesoporous silica Co-Zn/SBA-15 catalysts were prepared by incipient wetness impregnat...
à®®à¯à®´à¯ விளகà¯à®•à®®à¯
Saved in:
| தலைமை எழà¯à®¤à¯à®¤à®¾à®³à®°à¯: | |
|---|---|
| வடிவமà¯: | Undergraduates Project Papers |
| வெளியீடபà¯à®ªà®Ÿà¯à®Ÿà®¤à¯: |
2010
|
| பகà¯à®¤à®¿à®•à®³à¯: | |
| நிகழà¯à®¨à®¿à®²à¯ˆ அணà¯à®•à®²à¯: | http://iportal.ump.edu.my/lib/item?id=chamo:57006&theme=UMP2 http://iportal.ump.edu.my/lib/item?id=chamo:57006&theme=UMP2 http://umpir.ump.edu.my/3345/1/CD5493_MUHAMMAD_ZAKWAN_BIN_A.RAZAK.pdf |
| கà¯à®±à®¿à®¯à¯€à®Ÿà¯à®•à®³à¯: |
கà¯à®±à®¿à®šà¯à®šà¯Šà®²à¯ இணை
கà¯à®±à®¿à®¯à¯€à®Ÿà¯à®•à®³à¯ இலà¯à®²à¯ˆ, இநà¯à®¤ கà¯à®±à®¿à®šà¯à®šà¯Šà®²à¯à®²à¯ˆ à®®à¯à®¤à®²à®¿à®²à¯ பதிவ௠செயà¯à®¯à¯à®™à¯à®•à®³à¯!
|
| தொகà¯à®ªà¯à®ªà¯: | The influence of promoter (Zn) on the physiochemical and catalytic properties of mesaporous silica Co/SBA-15 catalysts for the Fischer-Tropsch (FT) synthesis was investigated. SBA-15 was synthesized as support. The mesoporous silica Co-Zn/SBA-15 catalysts were prepared by incipient wetness impregnation method. Cobalt nitrate and zinc nitrate were used as sources of metal that are introduced onto catalysts with same cobalt loading (15 wt %) and different zinc loading (5 wt %, 10 wt%, 15 wt %) The characterization of catalysts was performed by using Fourier transform infrared (FTIR), scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). The results for FTIR were identification of Si-O-Si functional group indicating the absortion of silica inside SBA-15 support. Beside that, the identification of metal inside SBA-15 was determined by comparing the pure SBA-15 with the incorporated metal on SBA-15. For SEM analysis the image shows that the rope like domain aggregated to wheat-like microstructure. For this research, the characterization of the catalyst by selecting Zn as promoter have quiet similar characterization with noble metal that have been already investigate. |
|---|