Self-Healing Behaviour of Pre-Cracked Pofa-Concretes in Different Curing Conditions
The investigation of the effect of curing conditions on self-healing of pre-cracked concrete containing palm oil fuel ash (POFA)-concrete is presented. Concrete grade 30 was used and POFA cement replaced 10%, 20% and 30% of the total weight of ordinary Portland cement [1].The compressive strength w...
à®®à¯à®´à¯ விளகà¯à®•à®®à¯
Saved in:
| தலைமை எழà¯à®¤à¯à®¤à®¾à®³à®°à¯à®•à®³à¯: | , , |
|---|---|
| வடிவமà¯: | கடà¯à®Ÿà¯à®°à¯ˆ |
| வெளியீடபà¯à®ªà®Ÿà¯à®Ÿà®¤à¯: |
Faculty Mechanical Engineering, UMP
2014
|
| பகà¯à®¤à®¿à®•à®³à¯: | |
| நிகழà¯à®¨à®¿à®²à¯ˆ அணà¯à®•à®²à¯: | http://dx.doi.org/10.15282/jmes.7.2014.22.0120 http://dx.doi.org/10.15282/jmes.7.2014.22.0120 http://umpir.ump.edu.my/8984/1/Self-Healing%20Behaviour%20Of%20Pre-Cracked%20Pofa-Concretes%20In%20Different%20Curing%20Conditions.pdf |
| கà¯à®±à®¿à®¯à¯€à®Ÿà¯à®•à®³à¯: |
கà¯à®±à®¿à®šà¯à®šà¯Šà®²à¯ இணை
கà¯à®±à®¿à®¯à¯€à®Ÿà¯à®•à®³à¯ இலà¯à®²à¯ˆ, இநà¯à®¤ கà¯à®±à®¿à®šà¯à®šà¯Šà®²à¯à®²à¯ˆ à®®à¯à®¤à®²à®¿à®²à¯ பதிவ௠செயà¯à®¯à¯à®™à¯à®•à®³à¯!
|
| தொகà¯à®ªà¯à®ªà¯: | The investigation of the effect of curing conditions on self-healing of pre-cracked concrete containing palm oil fuel ash (POFA)-concrete is presented. Concrete grade 30
was used and POFA cement replaced 10%, 20% and 30% of the total weight of ordinary Portland cement [1].The compressive strength was tested after 7, 28, 60 and 90 days
cured in water in order to investigate the strength development of the POFA-concretes. In addition, the pre-crack (hairline crack) concrete was examined under compression load to determine the effectiveness of self-healing POFA-concretes after different curing conditions. Four types of curing condition, namely air, room temperature, wet and dry, and water curing were tested. An ultra-pulse velocity (UPV) test was performed after 7, 28, 60 and 90 days of curing to monitor the self-healing progress in the POFA-concrete. The results show that POFA-concrete witha 20% replacement level
recorded the highest compressive strength. It was also revealed that the UPV readings increased significantly with increased curing age. The results showed that the selfhealing ability of pre-cracked POFA-concrete at 10% replacement level increases significantly for the water curing condition. From these findings, the optimum POFA
replacement level was recorded at 20% for the strength, while inclusion of a 10% POFA replacement level was appropriate for self-healing concrete |
|---|