Failure Analysis On TIG Weldment
This project is discussed about failure analysis on Tungsten Inert Gas (TIG) weldment. The objective of this failure analysis project is to determine and identify the type of failure that most occur in TIG welding. The parameter that contribute to this failure occur also will be study and identify....
Saved in:
| Main Author: | |
|---|---|
| Format: | Monograph |
| Published: |
UTeM
2008
|
| Subjects: | |
| Online Access: | http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=fullDisplayRetriever.jsp&szMaterialNo=0000048790 http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=fullDisplayRetriever.jsp&szMaterialNo=0000048790 http://eprints.utem.edu.my/1375/1/Failure_Analysis_On_TIG_Weldment_-_Ahmad_Muslim_Othman_-_TS227.A35_2008_24_Pages.pdf http://eprints.utem.edu.my/1375/2/Failure_Analysis_On_TIG_Weldment_-_Ahmad_Muslim_Othman_-_TS227.A35_2008.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This project is discussed about failure analysis on Tungsten Inert Gas (TIG) weldment. The objective of this failure analysis project is to determine and identify
the type of failure that most occur in TIG welding. The parameter that contribute to this failure occur also will be study and identify. This failure analysis project will be
held in machine syop laboratory at Universiti Teknikal Malaysia, Melaka and the machine that will be used is Tungstent Inert Gas welding. The same material such as
mild steel will be used to do the joining process, and this action will be repeated and all the failure or defects that occur during this process will be recorded. The failure
that expected to be occurring during this joining process is root crack, porosity, slag inclusion, and lack of root fusion. These all defects or failures will be analyzed using
Fault Tree Analysis (FTA) and fishbone or cause and effect diagram. This method is used to determine the causes for this failure occur and recommendation for proper welding technique and proper parameter setting for this machine can be suggested after that. |
|---|