The Influence Of Cu-Reinforced Aluminium Metal Matrix Composite To The Mechanical Properties, Corrosion Resistance And Microstructure
The objective of this project is to the study the mechanical characteristic alteration, to investigate on corrosion rate and to carry out observation on the microstructure due to the different filJer loading of reinforcement. The composition of reinforcement material which is cooper will be added...
Saved in:
| Main Author: | |
|---|---|
| Format: | Monograph |
| Published: |
UTeM
2009
|
| Subjects: | |
| Online Access: | http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=fullDisplayRetriever.jsp&szMaterialNo=0000052182 http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=fullDisplayRetriever.jsp&szMaterialNo=0000052182 http://eprints.utem.edu.my/3789/1/The_Influence_Of_Cu-Reinforced_Aluminium_Metal_Matrix_Composite_To_-_24_pages.pdf http://eprints.utem.edu.my/3789/2/The_Influence_Of_Cu-Reinforced_Aluminium_Metal_Matrix_Composite_To.........pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The objective of this project is to the study the mechanical characteristic alteration, to
investigate on corrosion rate and to carry out observation on the microstructure due
to the different filJer loading of reinforcement. The composition of reinforcement
material which is cooper will be added to Aluminum 390. It wiJl be in the
verification into 0, 2, 5 and 8wt0/o. In addition, preparation of this sample is complete
through casting process tag along with parameter of addition material specification as
it's confirmed. Next, the cutting process is performing by following the standard size
for remaining tests which is confinned. Then, the metal block will going through
with heat treatment process namely solution heat treatment and artificial ageing.
Whilst the sample is produced, hardness test (ASTM El8-03), corrosion test (ASTM
G61) and microstructure observation is perform. Based on the acquired data, the
comparison will be performs between Aluminum 390 data and sample MMC data
which is produced. The achieve result, for hardness test the value of HRB is increase
together with expansion of copper and corrosion rate become higher with increases
of copper percentage. If referred on theory, the achieve properties on this experiment
has successfuJly fuJfill objective of the project because theory authentication with
experiment is parallel. |
|---|