Analysis of cracked in thick-tube using finite element modelling
Most engineering failure began with cracks. Crack may caused by material defect, discontinuities in geometry or damage in service. Thus, Fracture Mechanics is introduced as a method for predicting failure of a surface containing a crack. This project is focusing on pre-existing crack with assumption...