Producing of cobait chromium molybdenum (CoCrMo) foam by replication method
Cobalt Chromium Molybdenum (CoCrMo) generally known as a highly resistant to corrosion and wear performance. The aim of this paper is to producing CoCrMo foam that will be given to consider the properties of CoCrMo foam after sintering process. The CoCrMo slurry was produced by mixing CoCrMo powder...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Published: |
2014
|
| Subjects: | |
| Online Access: | http://eprints.uthm.edu.my/5899/ http://eprints.uthm.edu.my/5899/4/Producing_Of_CobaIt_Chromium_Molybdenum_x.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Cobalt Chromium Molybdenum (CoCrMo) generally known as a highly resistant to corrosion and wear performance. The aim
of this paper is to producing CoCrMo foam that will be given to consider the properties of CoCrMo foam after sintering process. The CoCrMo slurry was produced by mixing CoCrMo powder with Polyethylene Glycol (PEG), Carboxyl Methyl Cellulose (CMC) and distilled water. Then, polymeric foam template was impregnated in CoCrMo slurry and dried at room temperature. Sintering was carried out in a high temperature tube furnace at 1300°C. The microstructure of the CoCrMo foam produced was observed by using Energy
Dispersive X-ray Spectroscopy (EDS) and X-Ray Diffraction (XRD). The detected element in CoCrMo foam that was analyse
by EDS were Cr, Mo, Co, Mn, C, 0, Al, Si and Ca. Then the compound that detected by XRD testing was Cobalt Nitride. |
|---|