The rubber elasticity of poly (N-isopropylacrylamide) hydrogel networks
We report here on the characterization of classical bulk poly (N-isopropylacrylamide) (PNIPAAm) hydrogel networks. The classical PNIPAAm hydrogels were prepared from N-isopropylacrylamide (NIPAAm) as a main monomer and N,N-methylenebisacrylamide (MBAAm) as a crosslinker. The viscoelastic character o...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Published: |
2013
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/40838/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | We report here on the characterization of classical bulk poly (N-isopropylacrylamide) (PNIPAAm) hydrogel networks. The classical PNIPAAm hydrogels were prepared from N-isopropylacrylamide (NIPAAm) as a main monomer and N,N-methylenebisacrylamide (MBAAm) as a crosslinker. The viscoelastic character of bulk hydrogels was examined using rheological measurements under frequency sweep mode (20 °C). A range of frequency, ? from 0.1 to 100 rad/s, was employed as this is a typical range for rubber plateau. Within this range, almost frequency independent of storage moduli (G'; ~ 104 Pa as a function of hydrogel compositions were obtained. Indeed, the perfect soft-rubbery behaviour of PNIPAAm hydrogels could be confirmed and thus enabled the estimation of mesh size. Interestingly, the mesh size rubbery hydrogels determined from rheological data was in a good agreement to that from swelling experiments (~ 4 to 9 nm). |
|---|