Effect of carbonization heating rate on CO2 separation of derived carbon membranes
High performance carbon hollow fiber membranes (CHFM) for CO2 separation were prepared by manipulating of carbonization heating rates under a N2 atmosphere. During heat treatment process, carbonization of the polymeric hollow fiber membrane was conducted up to 650 °C and in the range of 1–9 °C/min f...