Effect of Electrodeposition Parameters on the Microstructure and Corrosion Behavior of DCPD Coatings on Biodegradable Mg-Ca-Zn Alloy
In this study, DCPD (Brushite, CaHPO4.2H2O) coatings were prepared on the surface of a Mg-Ca-Zn alloy using different current density (0.15-1.2 mA/cm2) and deposition time (5-90 min). The results revealed that DCPD with needle-like morphology was observed for the current density between 0.15 and 0.4...